Karakteristik Silika Sekam Padi Kabupaten Cilacap Dengan Menggunakan Ekstraksi KOH Dan HCl

Nur Fitry Indah Mawarti, Riza Ma'riffathur Ramadhan, Saddam Libertyan, Dodi Satriawan

Abstract


This research aims to conduct an initial analysis of the characteristics of rice husk silica to be used as a membrane for purifying used cooking oil. Rice husks were obtained from Cilacap district. Rice husks are pyrolyzed at 650 0C for 6 hours until rice husk ash is produced. The rice husk ash is ground to a size of 50 mesh. Then 50 grams of rice husk ash was weighed and washed with 1 L of distilled water at a temperature of 80 0C. The washed ash was then extracted with 1 L of 5% KOH for 2 hours at a temperature of 75 0C. The silica extraction was divided into 5 and 10% HCL was added to obtain a pH of 4, 5, 6, 7, and 8. The analysis carried out included rice husk ash yield analysis, silica yield, water content analysis, and iodine absorption analysis. The best results were obtained at pH 8 in the silica yield obtained, the water content at pH 6 was 7.4%, and the iodine absorption capacity at pH 8 was 1271.71%.

Keywords


rice husk ash; silica;characteristics of silica

Full Text:

PDF

References


Agung M, G. F., Hanafie Sy, M. R., & Mardina, P. (2013). Ekstraksi Silika Dari Abu Sekam Padi Dengan Pelarut KOH. Konversi, 2(1), 28. https://doi.org/10.20527/k.v2i1.125.

Amalia, R. F., Purwaningsih, H., Susanti, D., & Pratiwi, V. M. (2020). Analisis Pengaruh Rasio Pelarut Etanol Terhadap Kinerja Nanopartikel Silika Mesopori dari Sekam Padi sebagai Material Pengantar Obat. Jurnal Teknik ITS, 9(1), 66–71. https://doi.org/10.12962/j23373539.v9i1.50395.

Badan Pusat Statistika. (2020). Statistik Luas Panen dan Produksi Padi. Berita Resmi Statistik, 2(16), 1–12. https://www.bps.go.id/pressrelease/2020/10/15/1757/luas-panen-dan-produksi-padi-pada-tahun-2020-mengalami-kenaikan-dibandingkan-tahun-2019-masing-masing-sebesar-1-02-dan-1-02-persen-.html.

Dewi Umaningrum, Mujiyanti, D. R., & Nurmasari, R. (2019). Adsorpsi Pb(Ii) Oleh Asam Humat Terimobilisasi Pada Hibrida Merkapto Silika Dari Abu Sekam Padi. Paper Knowledge . Toward a Media History of Documents, Ii, 20–26.

Fatriansyah, J. F., Situmorang, F. W., & Dhaneswara, D. (2018). Ekstraksi silika dari sekam padi: metode refluks dengan naoh dengan pengendapan menggunakan asam kuat (hcl) dan asam lemah (CH3COOH). Prosiding Seminar Nasional Fisika Universitas Riau Ke-3, 5(1), 123–127.

Gumirat, M. I. I., & Satriawan, D. (2021). Analisis Kalor Biobriket Sekam Padi Pada Variasi Perekat Dan Variasi Tekanan. Seminar Nasional Terapan Riset Ino Atif (SENT NOV) Ke-VII, 598–604.

Hardyanti, I. S., Nurani, I., Hardjono HP, D. S., Apriliani, E., & Wibowo, E. A. P. (2017). Pemanfaatan Silika (SiO2) dan Bentonit sebagai Adsorben Logam Berat Fe pada Limbah Batik. JST (Jurnal Sains Terapan), 3(2). https://doi.org/10.32487/jst.v3i2.257.

Hayati, D., Pandoyo, & Azmiyawati, C. (2017). Pengaruh Variasi Jenis Asam terhadap Karakter Nanosilika yang. Journal Sains Dan Aplikasi, 20(1), 1–4.

Hidayatulloh, C. Y., Iskandar, A. S., Al-ayubi, S., Permanasari, A. R., & Kunci, K. (2021). Kajian Pustaka Pemanfaatan Silika Sekam Padi sebagai Aerogel Adsorben untuk Menurunkan Kandungan Logam pada Air. Industrial Research Workshop and National Seminar, 779–784.

Masrofah, I. (2017). Kajian Pemanfaatan Silika dari Sekam Padi dalam Pengolahan Limbah Tekstil. Jurnal Media Teknik Dan Sistem Industri, 1, 60. https://doi.org/10.35194/jmtsi.v1i0.61.

Meliyana, M., Rahmawati, C., & Handayani, L. (2019a). Sintesis Silika Dari Abu Sekam Padi Dan Pengaruhnya Terhadap Karakteristik Bata Ringan. Elkawnie: Journal of Islamic Science and Technology, 5(2), 164. https://doi.org/10.22373/ekw.v5i2.5533.

Meliyana, Rahmawati, C., & Handayani, L. (2019b). Sintesis Nano Silika Dari Abu Sekam Padi Dengan METODE SOL GEL. Prosiding Seminar Nasional Multidisiplin Ilmu Universitas Asahan Ke-3, 800–807.

Ndoen, M. C. ., & Wogo, H. E. (2020). Optimasi Volume Larutan Prekursor Natrium Silikat Hasil Pengolahan Abu Sekam Padi Terhadap Kelenturan Plastik Komposit Silika Terimobilisasi Edta-Ag Dan Kitosan. Jurnal Saintek Lahan Kering, 3(1), 16–19. https://doi.org/10.32938/slk.v3i1.1025.

Puspayana, D. R., & Damayanti, A. (2013). Pengolahan Limbah Cair Industri Pewarnaan Jeans Menggunakan Membran Silika Nanofiltrasi Aliran Cross Flow untuk Menurunkan Kadar Nitrat dan Amonium. Jurnal Teknik Pomits, 2(2), 113–117.

Rosalia, R., Asmi, D., & Ginting, E. (2016). Preparasi dan Karakterisasi Keramik Silika (SiO 2 ) Sekam Padi dengan Suhu Kasinasi 800-1000 C. Jurnal Teoro Dan Aplikasi Fisika, 04(01), 101–106.

Salman, M. N., Krisdiyanto, D., Khamidinal, K., & Arsanti, P. (2015). Preparasi Katalis Silika Sulfat Dari Abu Sekam Padi Dan Uji Katalitik Pada Reaksi Esterifikasi Gliserol Dengan Anhidrida Asam Asetat. Reaktor, 15(4), 231–240. https://doi.org/10.14710/reaktor.15.4.231-240.

Sandya, Y., Prihantono, & Musalamah, S. (2019). Penggunaan Abu Sekam Padi Sebagai Pengganti Semen Pada Beton Geopolimer. Jurnal Pendidikan Teknik Bangunan Dan Sipil, 5(2), 59–63. https://jurnal.unimed.ac.id/2012/index.php/eb/issue/view/1755.

Sapei, L., Padmawijaya., Karsono, S., Sutejo, A., & Theresia, L. (2015). Karakterisasi Silika Sekam Padi Dengan Variasi Temperatur Leaching Menggunakan Asam Asetat. Jurnal Teknik Kimia, 9(2), 38–43.

Satriawan, D., Santoso, A., & Widianingsih, B. (2021). Analisis Kuantitatif Pengaruh Waktu Karbonisasi Dan Kosentrasi Koh Pada Pembuatan Karbon Aktif Sekam Padi. Seminar Masional Terapan Riset Inovatif (SENTRINOVE), 7(2), 605–612.

Sulaeman, A. S., Arjo, S., & Maddu, A. (2019). Sintesis dan Karakterisasi Silicon Carbide (SiC) dari Sekam Padi Menggunakan Metode Reduksi Magnesiotermik. Jurnal Fisika FLUX, 1(1), 47. https://doi.org/10.20527/flux.v1i1.6146.




DOI: http://dx.doi.org/10.31258/dli.11.1.p.65-68

Refbacks

  • There are currently no refbacks.


Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.